Hydriding processes of Mg and Zr alloys by reactive milling

Mulas, Gabriele Raimondo Celestino and Schiffini, Liliana and Tanda, Giusy and Cocco, Giorgio (2004) Hydriding processes of Mg and Zr alloys by reactive milling. Journal of Materials Science, Vol. 39 (16-17), p. 5251-5254. eISSN 1573-4803. Article.

Full text not available from this repository.

DOI: 10.1023/B:JMSC.0000039221.13779.2e


Mechanically alloyed Mg2/Ni/Ni nano-composite and Zr55Cu30Ni5Al10 amorphous powders were hydrogen charged at constant pressure under ball milling. While the Mg-based samples were able to absorb large amount of hydrogen under static conditions, and from the very onset of the mechanical treatment, an incubation milling period was needed for the hydrogen activation in the case of the amorphous sample. A progressively decreasing rate characterizes the process kinetics in the case of Mg2Ni/Ni, whereas a self increasing sigmoid trend was observed for the multicomponent Zr alloy, which showed structural demixing phenomena in the absorption course. Irrespective of the system, the maximum absorption rate was strongly dependent on the milling intensity (Watt•g-1). The hydriding rate (mole•g-1s-1) and the mechanochemical yield (mole•Joule-1) were used to compare the processes on an absolute scale. In the case of Mg-based alloy, comparison was also made between mechanically induced and thermally (static) activated hydriding processes. Attempt was also made to work out the hydrogen atoms absorbed at the ball-hit event.

Item Type:Article
ID Code:2705
Uncontrolled Keywords:Magnesium, zirconium, absorption, structural demixing phenomena
Subjects:Area 03 - Scienze chimiche > CHIM/02 Chimica fisica
Divisions:001 Università di Sassari > 01 Dipartimenti > Chimica
Publisher:Springer Netherlands
Additional Information:Paper presented at the International Conference on Mechanochemistry and Mechanical Alloying (INCOME 2003), Braunschweig, Germany, 7-11 September 2003.
Deposited On:18 Aug 2009 10:08

I documenti depositati in UnissResearch sono protetti dalle leggi che regolano il diritto d'autore

Repository Staff Only: item control page